AbstractThe effects of a pretreatment of polyester (PET) yarns with a strongly interacting solvent such as dimethylformamide (DMF) on vinyl monomer incorporation were investigated. When the DMF pretreatment is carried out at high temperatures (above 120°C), the swollen PET structure is stabilized by solvent‐induced secondary crystallization. This substrate is highly suitable for the incorporation of vinyl monomers.In situpolymerization of vinyl monomers in DMF‐treated PET was investigated using chemical and γ‐irradiation polymerization techniques, both in the presence and in the absence of excess monomer outside the PET fibers. When polymerization was carried out in a system in which a constant supply of free radicals was available from the outside of the PET fibers, lower initiator concentrations and smaller γ‐irradiation doses were necessary. These results are attributed to a low efficiency of the initiator inside the PET fiber due to mobility restrictions. Water uptake and moisture regain of PET yarns containing poly(hydroxyethyl methacrylate) and poly(acrylic acid) were also investigated. When most of the vinyl polymer was inside the PET fiber, water absorption was limited. The changes in mechanical properties of the PET yarns resulting from the DMF pretreatment were partially reversed byin situpolymerization of viny
展开▼