AbstractMedium weight twill fabrics constructed from cotton and cotton blended with polyester and/or wool were analyzed under nitrogen by three thermoanalytical techniques. Fabrics were tested both before and after treatment with tetrakis(hydroxymethyl)phosphonium sulfate (THPS), urea, and trimethylolmelamine. The presence of all fibers was distinguishable in differential scanning calorimetric analysis (DSC) of untreated fabrics; the relative positions of the endothermic, decomposition peak temperatures were only slightly changed. After flame‐retardant (FR) treatment, the blended cotton and wool fibers were altered. Both fibers decomposed as exotherms during DSC analysis. These data supported earlier microscopical, X‐ray evidence that wool fibers were actually reacting with the FR treatment. The two DSC peaks for polyester polymer melting and decomposing remained unaffected by either blending with other fibers or the presence of the FR finish on the fabric. There was excellent agreement between DSC peak temperatures and the temperature of maximum rate of weight loss obtained from thermogravimetric analysis (TGA). Blending cotton with either of these fibers increased the residue measured after TGA. The increased residue correlated with increased flame resistance as measured by the 45° angle, edge‐ignition burning rat
展开▼