AbstractThe effects of crosslinking upon the dynamic mechanical properties and swelling behavior of poly(acrylic acid) (PAA) have been studied. Materials were prepared by the free radical copolymerization of acrylic acid with varying amounts of the tetrafunctional monomer allyl acrylate (ALA). The results indicated a linear dependence of the glass‐transition temperature (Tg) on composition,Tgincreasing by ∼43°C over the mole fraction rangeX= 0−0.37 ALA. Room temperature (25°C) modulus values, as determined by both dynamic and compression methods, were inversely proportional to the initial concentration of ALA. The degree of network formation has been characterized in terms of the molecular weight between crosslinksMc, and the influence of this parameter on the swelling ratio was di