Crystallization and melting behaviors of poly(aryletheretherketone) (PEEK) on origin of double melting peaks

机译：Crystallization and melting behaviors of poly(aryletheretherketone) (PEEK) on origin of double melting peaks

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

AbstractThe crystallization and melting behaviors of poly(aryletheretherketone) (PEEK) films were investigated, using differential scanning calorimetry and metallurgy concepts. The shape of the time–temperature–transformation (TTT) diagram, established for PEEK, results from both nucleation and growth phenomena. The double melting behavior exhibited by isothermally crystallized PEEK samples are discussed through the TTT diagram and the influence of the thermal history in the molten state. The upper melting peak arises first and the lower melting peak is developed later. The location of such a second endotherm is shifted toward the higher temperature with increasing either the crystallization temperature or the annealing time while the location of the upper melting peak seems to be unchanged. The double melting behavior is related to a bimodal distribution in size and/or perfection of lamellae developed in a two‐step crystallization. With increasing temperature and/or annealing time in the molten state, the pattern of the endothermic curves is modified. The observed changes are discussed through two origins: the progressive disappearance of remnants of the former crystals and a thermal degradation leading to a cross‐linking of the polymer. © 1994 John WileyS

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号