Effects of heat treatment on various properties of organic-inorganic hybrid silica derived from phenyltriethoxysilane

机译：Effects of heat treatment on various properties of organic-inorganic hybrid silica derived from phenyltriethoxysilane

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Microparticles of organic-inorganic hybrid silica derived from a tri-functional ethoxysilane (phenyl-triethoxysilane (PTES)) still have non-negligible amount of silanol (Si-OH) moiety after it is solidified in its outside appearance. Those residual silanol moiety formed in the Stober process resumes further polycondensation in a heat treatment at temperatures above 250 degrees C. The rate of the polycondensation reaction of the residual moiety is dominantly influenced by the temperature at which the heat treatment was carried out. Heating at 300 degrees C for 192 h completes the polycondensation and entirely eliminates the residual silanol groups. The completion of polycondensation of the residual silanol is detected by visually observable insolubility of the heat-treated powder in acetone. The elimination of the silanol moiety due to the completion of the polycondensation is shown by the complete absence of the infrared absorbance corresponding to hydroxyl groups at approximately 950 cm(-1). The completion of the polycondensation leads to densification of the siliceous polymeric network as indicated by the prevention of amphiphilic organic solvent (e. g., N,N-dimethylformamide) from permeating into the bulk matrix of the organic-inorganic hybrid silica. The thermogravimetric measurement shows that phenyl groups directly bonded to Si remains intact at the temperature region (approximate to 300 degrees C) wherein the polycondensation reaction of the residual silanol groups is strongly promoted. (C) 2014 Elsevier B.V. All rights reserved.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号