AbstractThe changed viscoelastic properties of the epoxy resin‐acid anhydride system, Epikote 834‐HHPA, are followed to the gel point at 130, 140, and 150°C with a dynamic viscoelastometer. The viscosity increases with curing time through two inflections designated A and B. The point A is interpreted (from the reference to the chemical changes reported in the previous paper) as the termination of the initial stage of this curring reaction, and point B coincides with the gel point determined by the torsion method. The resonance frequency remains constant value up to the point B, followed by a rapid increase. The extents of reaction for epoxide, anhydride, and initial OH are 15, 45.8, and 100 at the point A; 27.8, 63.7, and 100 at the point B, respectively. The apparent activation energies for viscosity are 7.5 kcal/mole for the resin mixture before curing, 10.5 kcal/mole for point A, 48.8 kcal/mole for point B (gel point). The overall apparent activation energies of this curing reaction are obtained from the Arrhenius plots for the curing time required for the resin mixture to reach the state of the points A and B; these values were 8.9 kcal/mole for point A and 16.2 kcal/mole for poi
展开▼