首页> 外文期刊>Journal of thermal analysis and calorimetry >Exploration of high pressure phase in LaGaO3 and LaCrO3
【24h】

Exploration of high pressure phase in LaGaO3 and LaCrO3

机译：Exploration of high pressure phase in LaGaO3 and LaCrO3

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Structural phase transitions upon the application of high pressure in LaGaO3 and LaCrO3, which were prospected from diffraction and thermal analyses of phase transition under ambient pressure, were discovered by using high-pressure X-ray diffraction. It was revealed that the crystal structures of LaCrO3 and LaGaO3 changed completely from that of orthorhombic distorted perovskite to that of a rhombohedral distorted one upon the application of pressure higher than 5.4 and 3.0 GPa, respectively, at room temperature. The variation of lattice constants with pressure was investigated for the high-pressure rhombohedral phases of LaCrO3 and LaGaO3 and isothermal compressibility was estimated. The variation of lattice constants with pressure at room temperature in the high-pressure rhombohedral phase was compared with that with temperature at ambient pressure in high-temperature rhombohedral phase. It was found that the application of pressure decreased the crystal symmetry, which was opposite to the result in the case of increasing the temperature.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号