>Characterization of physical aging of poly(methyl methacrylate) powders by a novel high pressure sorption technique
【24h】
Characterization of physical aging of poly(methyl methacrylate) powders by a novel high pressure sorption technique
展开▼
机译：Characterization of physical aging of poly(methyl methacrylate) powders by a novel high pressure sorption technique
AbstractHigh pressure CO2sorption isotherms were measured at 35°C in previously dilated PMMA microspheres, which were subsequently aged in vacuum at 35°C. The dilation was induced by preswelling with high activity methanol vapor at 13°C, or alternatively with CO2at a pressure of 20 atm and a temperature of 5°C. The state of the samples during long‐term aging was probed by rapid and intermittent determination of complete high pressure CO2isotherms. The dilation increased the sorption levels observed in the sorption experiments compared to those observed in untreated samples and, as the aging time increased, the sorption level progressively decreased. The isotherms under all conditions were well described by the dual mode sorption model. The observed time dependence of the isotherms was successfully described by confining all changes in sorption capacity to a systematic decay of the Langmuir capacity parameter. The equilibrium parameters of the model, however, were essentially unaffected by the preswelling and aging hist
展开▼