首页> 外文期刊>journal of applied polymer science >A fatigue crack initiation map for polycarbonate
【24h】

A fatigue crack initiation map for polycarbonate

机译：A fatigue crack initiation map for polycarbonate

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

AbstractThe mechanisms of fatigue crack initiation for various stress levels and thicknesses have been determined for single‐edge notched specimens of polycarbonate and used to assemble a map. Three basic fatigue crack initiation mechanisms were identified and named as cooperative ductile (the damage zone formed ahead of crack consisting of yielded material), solo‐crack brittle (very little damage zone development), and cooperative brittle (identified as a cloud of microcracks or crazes that developed at the notch tip). With a given applied stress and within the same failure mechanism, the values of the number of cycles to crack initiation decrease with increase in thickness. The transition from cooperative ductile to solo‐crack brittle initiation mechanisms is sudden with increasing thickness. Transition from cooperative ductile to cooperative brittle with decreasing stress was less well defined. Regions where combinations of mechanisms were observed are also identified in the map. © 1993 John WileySon

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号