首页> 外文期刊>ISIJ International >Microstructures and age hardening characteristics of direct quenched Cu bearing HSLA steel
【24h】

Microstructures and age hardening characteristics of direct quenched Cu bearing HSLA steel

机译：Microstructures and age hardening characteristics of direct quenched Cu bearing HSLA steel

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Microstructures and age hardening characteristics of 0.04C-3.5Ni-0.6Cr-1.8Cu-0.4Mo-0.03Nb Cu bearing HSLA steel menufactured by reheat quenching (RQ) and direct quenching (DQ) processes, were investigated. Especially, the effect of DQ treatment on quenched microstructures and niobium carbide and epsilon-Cu precipitation were examined. A finer quenched microstructure was obtained in DQ processed steel compared with RQ processed steel, due to the heavily deformed austenite introduced by DQ. In DQ processed steel, lath and block sizes of martensite decreased and internal dislocation density increased with the increase of austenite deformation in the non-recrystallization region. Hence, the strength of quenched DQ steel increased with the amount of deformation in non-recrystallization region. epsilon-Cu precipitation characteristics in the aging stage changed very sensitively to the quenched microstructures. The size and growth rate of epsilon-Cu precipitate decreased with the amount of deformation in the non-recrystallization region, because heavily dislocated structure supplied more preferred nucleation sites of epsilon-Cu precipitates and retarded the precipitate growth. Also, DQ process affected the niobium carbide precipitation in this steel. In RQ steel, most of niobium precipitated as a coarse carbide in the reheating stage for austenitization. Whereas, in DQ steel, most of niobium precipitated very finely in the aging stage and thus highly contributed to the increase of the strength and tempering resistance. Therefore, it was concluded that DQ processed steel had higher strength and tempering resistance than RQ processed steel due to the finer epsilon-Cu and niobium carbide precipitates.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号