首页> 外文期刊>Corrosion: The Journal of Science and Engineering >Passivities of Steels Weathered for Nine Years
【24h】

Passivities of Steels Weathered for Nine Years

机译：Passivities of Steels Weathered for Nine Years

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

A carbon steel (CS) and a weathering steel (WS) were weathered in a temperate urban atmosphere for nine years. Phases of their rust layers were examined. Their corrosion behaviors were probed in aerated, neutral 0.5 M sodium sulfate (Na_2SO_4) bulk solution at room temperature using the potentiodynamic anodic polarization technique. Passivities by the layers with, a corrosion rate of 0.05 mm/y or less at the corrosion potential of-150 mV upsilon s saturated calomel electrode (SCE) or higher were observed, but they survived temporarily in the solution for 20 h and 5 hon the WS and CS covered with magnetite plus hematite phases, respectively, and 4 h and 1 hon the WS and CS with lepidocrocite plus goethite phases, respectively. They degraded with continued immersion in the solution accompanied by decreasing corrosion potential, finally near the active corrosion of bare steels. The passivities are under diffusion control of the iron ion dissolved from the base steels through the water in open pores of the layers but degrade by thinning and pore-opening of the layers under hydra-tion and reductive reactions of the layers. The passivities are strengthened by integration and pore-sealing of the layers with corrosion products of alloying elements for the WS and by more compact and less-reductive magnetite-containing phases than lepidocwcite-containing ones in the layers. These findings may be applied in the evaluation and improvement of corrosion resistance for WS.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号