首页> 外文期刊>journal of applied polymer science >Copolyesters. VII. Thermal transitions of poly(butylene terephthalate‐co‐isophthalate‐co‐adipate)s
【24h】

Copolyesters. VII. Thermal transitions of poly(butylene terephthalate‐co‐isophthalate‐co‐adipate)s

机译：Copolyesters. VII. Thermal transitions of poly(butylene terephthalate‐co‐isophthalate‐co‐adipate)s

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

AbstractThe copolyesters of 1,4‐butanediol, terephthalic acid, isophthalic acid, and adipic acid with different compositions were prepared by melt polycondensation. The intrinisic viscosity of the copolyesters was controlled to be about 0.7–1.0 dL/g. Their second‐run thermal properties were determined by DSC. The composition was found to be a major factor in the determination of the thermal transitions. The effect of the composition on the glass transition temperature and melt transition temperature was interesting. The glass transition temperature was found to be dependent mainly on the content of adipic acid. As the content of adipic acid increased, the glass transition decreased. When the content of terephthalic acid was not less than 35 mol based on the total diacid monomers, the melting temperature was dependent mainly on the content of terephtalic acid and increased with incrase of the content of terephthalic acid. When the content of terephthalic acid was less than 35 mol , the melt temperature of the copolyesters did not follow a simple rule. However, the effect of the composition on their melting enthalpy showed no simple trend. © 1994 John WileySon

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号