首页> 外文期刊>Corrosion: The Journal of Science and Engineering >Effect of Vacuum Brazing on Corrosion Resistance of UNS S31803 and UNS S31200 Duplex Stainless Steels
【24h】

Effect of Vacuum Brazing on Corrosion Resistance of UNS S31803 and UNS S31200 Duplex Stainless Steels

机译：Effect of Vacuum Brazing on Corrosion Resistance of UNS S31803 and UNS S31200 Duplex Stainless Steels

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Duplex stainless steel (DSS) has a combination of good mechanical strength and pitting corrosion resistance, but the precipitated brittle sigma (sigma) phase formed during cooling from a welding procedure will rapidly degrade its properties. to avoid the precipitation of secondary phases in the welds, the vacuum brazing effects on UNS S31803 and UNS S31200 DSS weld properties were investigated. Three fillers (copper foil and Ni-based alloys, BNi-3 and BNi-7) were used to evaluate the chemical composition influence on the corrosion resistance. In a nitrogen gas quench, a cooling rate of 0.85 deg C/s and sigma phase precipitation could be inhibited for the studied DSS. Under the quenched state, the weight loss was low for the UNS S31803 DSS dipped in 6 percent ferric chloride (FeCl_3) solution at 47.5 deg C for 24 h. however, the sigma phase precipitation in UNS S31803 increased as the cooling rate decreased. When the cooling rate decreased to 0.067 deg C/s, the UNS S31803 weight loss increased. Owing to the compositional difference between the filler and DSS, selective corrosion occurred at the interface of brazed joints soaked in 6 percent FeCl_3 solution for 24 h.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号