首页> 外文期刊>journal of applied polymer science >Structural changes of cellulose, wood, and paper under shear deformation and high pressure
【24h】

Structural changes of cellulose, wood, and paper under shear deformation and high pressure

机译：Structural changes of cellulose, wood, and paper under shear deformation and high pressure

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

AbstractStructural changes of wood and its components have been studied after shear deformation under high pressure (SDHP) at up to 6 GPa. Cellulose amorphization and chain depolymerization was observed. Approximately 30 of microcrystalline cellulose was soluble in water after a 360‐degree twist of the Bridgman anvils. The water‐insoluble part was re‐crystallized into cellulose II lattice. Repeated treatment applied to the nondissolved part of the sample, the so‐called cascade experiment, permits the dissolving of about 30 of the residual nondissolved material once again. Extraction with water, followed by 10 sodium hydroxide, allows almost complete dissolving of microcrystalline cellulose (98). Water‐soluble saccharides were studied by HPLC and13C NMR. It was found that destruction of the wood lignin network needs more severe treatment conditions than cellulose destruction does. Lignin domains in wood act as “grinding stones” during cellulose destruction. Long‐living lignin free radicals have been detected with EPR after SDHP.13C NMR CP/MAS spin diffusion studies showed that SDHP leads to separation of wood components into different biopolymer domains, which turns the system toward thermo‐dynamic equilibrium. SDHP does not permit achievement of initial compulsary compatibility of components in native wood. SDHP technique appears as a promising method for wood delignification and carbohydrate saccharification in the solid state without using harmful chemical reagents of solvents, which is important for technological safety and ecology. © 1994 Jo

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号