Corrosion Behavior of Deep Cryogenically Treated AISI 420 and AISI 52100 Steel

Wei Wang; Venkateswaran Srinivasan; Sri Siva

首页> 外文期刊>Corrosion: The Journal of Science and Engineering >Corrosion Behavior of Deep Cryogenically Treated AISI 420 and AISI 52100 Steel

【24h】

Corrosion Behavior of Deep Cryogenically Treated AISI 420 and AISI 52100 Steel

机译：Corrosion Behavior of Deep Cryogenically Treated AISI 420 and AISI 52100 Steel

获取原文

获取原文并翻译 | 示例

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相关主题

摘要

In this work, the impact of deep cryogenic and tempering treatment on the corrosion behavior of AISI 420 (UNS S42000) and AISI 52100 (UNS G52986) steel in 3.5 sodium chloride (NaCl) and sodium bicarbonate (NaHCO_3) + 0.25 NaCl solution was studied using open-circuit potential (OCP), potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS) measurements. The relationship of microstructure and the electrochemical response of differently treated samples was discussed. The results indicated that, compared with the conventional treatment, no significant modification of the electrochemical corrosion behavior after cryogenic treatments was observed. No passive behavior was observed for either AISI 420 or AISI 52100 in 3.5 NaCl, whereas it was observed in NaHCO_3 + 0.25 NaCl solution. Different effects of tempering treatment on the corrosion behavior between AISI 420 and AISI 52100 were observed due to different modifications of the microstructure during the tempering process. The amount of retained austenite has a critical role in determining the pitting resistance. The pitting resistance increased with the amount of retained austenite.

著录项

来源
《Corrosion: The Journal of Science and Engineering》 |2014年第7期|708-720|共13页
作者
Wei Wang; Venkateswaran Srinivasan; Sri Siva;
展开▼
作者单位

Department of Materials Engineering, The University of British Columbia, Vancouver, BC, Canada;

Cognizant Technologies Solutions, Tamilnadu, India;

Department of Mechanical Engineering, College of Engineering, Guindy, Anna University, Chennai 600 025, India;

展开▼
收录信息
原文格式 PDF
正文语种英语
中图分类金属腐蚀与保护、金属表面处理;
关键词
austenite; corrosion resistance; heat treatment; steel;

Corrosion Behavior of Deep Cryogenically Treated AISI 420 and AISI 52100 Steel

摘要

著录项

相关主题

期刊订阅