首页> 外文期刊>journal of applied polymer science >Preparation of polycarbonate/metal salt gas separation membranes
【24h】

Preparation of polycarbonate/metal salt gas separation membranes

机译：Preparation of polycarbonate/metal salt gas separation membranes

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

AbstractPolycarbonate (PC) membranes possess high O2/N2selectivity and mechanical strength, but have low gas permeability. In order to improve the pure PC membrane's gas permeability and selectivity of O2/N2, in this study we attempt to combine transition metal salts into the membrane to form a complex membrane. Tensile strength and elongation at break of the membrane are not significantly changed. The effect of casting solution composition and solvent evaporation time on morphology, gas permeability, and selectivity of O2/N2of PC membranes are studied. The gas permeabilities of PC/DMF/Metals membranes are significantly improved, as compared to those of pure PC membrane. For example, an oxygen permeability of 137 cm3(STP)‐cm/cm2‐sec‐cmHg and separation ratio of oxygen to nitrogen of 4.0 for PC/DMF/CuCl2membrane with PC/CH2Cl2/CuCl2/DMF = 17/3 mL/mL, and CuCl2/DMF = 0.1 g/mL, can be obtained. The FT–IR spectra and elementary analysis suggest that there is interaction among metal, DMF, and PC. © 1993 John WileyS

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号