首页> 外文期刊>Corrosion: The Journal of Science and Engineering >The Influence of Cold Plastic Deformation on Passivity of Ti-6Al-4V Alloy Studied by Electrochemical and Local Probing Techniques
【24h】

The Influence of Cold Plastic Deformation on Passivity of Ti-6Al-4V Alloy Studied by Electrochemical and Local Probing Techniques

机译：The Influence of Cold Plastic Deformation on Passivity of Ti-6Al-4V Alloy Studied by Electrochemical and Local Probing Techniques

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

The influence of cold plastic deformation on passivity of Ti-6Al-4V alloy (UNS R56400) was investigated by means of potentiodynamic polarization, Mott-Schottky analysis, atomic force microscopy, and scanning Kelvin probe force microscopy. The results showed that the cold working increased the passive current density. Mott-Schottky analysis revealed the n-type semiconducting behavior of the passive film. The donor density of the passive film was declined by increasing the film formation potential. On the other hand, work hardening increased the density of defects within the passive film, regardless of the applied potential. The Volta potential maps showed that a phase possesses lower surface potential compared to the beta, i.e., 38.6 mV. The plastic deformation decreased the surface potential of both phases; however, the relative nobility of the constituent phases had been slightly affected by cold working, i.e., 5 mV. The topographic results after immersion of the alloy in an aggressive acidic environment revealed that the Volta potential difference between alpha and beta was sufficient to make a more vulnerable to corrosion attacks.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号