首页> 外文期刊>Corrosion: The Journal of Science and Engineering >Self-Healing Behavior of Sodium Polyacrylate-Hydroxyapatite Coatings on Biodegradable Magnesium Alloy
【24h】

Self-Healing Behavior of Sodium Polyacrylate-Hydroxyapatite Coatings on Biodegradable Magnesium Alloy

机译：Self-Healing Behavior of Sodium Polyacrylate-Hydroxyapatite Coatings on Biodegradable Magnesium Alloy

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

The effect of the anionic polymer sodium polyacrylate (SPA) on the healing behavior of a hydroxyapatite (HAp) coating formed on Mg-3 mass Al-1 mass Zn (AZ31) alloy was examined. Static immersion tests of pre-scratched specimens and slow strain rate tensile (SSRT) tests were performed in simulated body fluid (Hanks' solution), for HAp-coated AZ31 with and without SPA. The static immersion tests revealed that the deposition of calcium phosphate (Ca-P) inside the scratches was enhanced by the presence of SPA, and the Ca-P layer deposited with SPA prevented local corrosion from the scratches. The SSRT tests revealed that the time to fracture of HAp-coated AZ31 increased by 45 in the presence of SPA. The fracture surface in the presence of SPA showed ductile regions to depths of 10 mu m to 20 mu m from crack initiation sites, and deeper regions showed a cleavage morphology. The cleavage morphology occurred directly from crack initiation sites in HAp-coated AZ31. The cleavage morphology suggested that hydrogen embrittlement occurred for AZ31 in Hanks' solution. The combination of SPA and HAp coating promoted the in situ healing of coating cracks upon formation. This helped to suppress corrosion under the cracks, which increased the time to fracture of HAp-coated AZ31.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号