首页> 外文期刊>Journal of thermal analysis and calorimetry >Barothermography and microstructure of the hypoeutectic and eutectic alloys in Al-Si system
【24h】

Barothermography and microstructure of the hypoeutectic and eutectic alloys in Al-Si system

机译：Barothermography and microstructure of the hypoeutectic and eutectic alloys in Al-Si system

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Differential barothermal analysis (DBA or HP-DTA) of the phase transformations in hypoeutectic Al-10 at. Si and eutectic Al-12 at. Si alloys was carried out at 100 MPa of argon pressure and at temperatures up to 700 A degrees C. Liquidus temperature of Al-10 at. Si is reduced during melting and crystallization by 3-4 A degrees C as compared with the atmospheric pressure data. Increase in the eutectic transformation L -> (Al) + Si temperature up to 580-581 A degrees C during heating was found for the Al-10 at. Si and Al-12 at. Si alloys. According to the barothermography data, a slight thermal effect at 553 A degrees C is detected for both alloys, which was identified as the decomposition of aluminum-based solid solution and precipitation of silicon particles. The improvement of silicon phase morphology for Al-10 at. Si and Al-12 at. Si alloys after hot isostatic pressing (HIP) at the pressure of 100 MPa and temperature of 550 A degrees C was found. No porosity in the alloy has been established after HIP treatment. After HIP thermal expansion, coefficients of the alloy are noticeably decreased by 25 (Al-10 at. Si) and 50 (Al-12 at. Si).

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号