AbstractDynamic mechanical properties of some epoxy matrix composites have been studied, comparing experimental data with theoretical models. The matrix in all composite samples was Shell Epon 828, a diglycidyl ether of bisphenol A, cured withmeta‐phenylenediamine. Fibrous composite samples were made with glass and graphite fibers. Particulate composite samples were made with glass microspheres, atomized aluminum, powdered silica, alumina, asbestos, mica, carbon black, and graphite. The dynamic elastic modulus and damping of these samples were measured at temperatures between 85° and 345°K by a free‐free flexural resonance technique. The dynamic modulus of parallel fiber composites follows the linear rule of mixtures for low fiber volume fractions; deviations from linearity at higher volume fractions appear to be due to defects caused by the sample fabrication technique. Dynamic moduli of the particulate composites conform, within experimental error, to the static modulus theory of Wu up to filler volume fractions of 0.35 to 0.40. Deviations from Wu's theory at higher volume fractions may be due to agglomeration of filler particles. The damping of particulate composites with quasi‐spherical filler particles appears to follow the rule of mixtures. In particulate composites with needle‐ and flake‐type fillers, and in fibrous composites, the fillers are more highly stressed; with more of the strain energy in the low‐damping fillers, overall damping is reduced. Damping greater than that attributable to the matrix and filler may be due to slippage at the interface between them. In addition to supporting Wu's theory of the elastic modulus of a particulate composite, this study demonstrates the utility of the nondestructive free‐free flexural resonance techniques for obtaining a large body of reliable data in a short time from relatively few small samples. This greatly facilitates the experimental testing of theoretical models and the evaluation of fillers, matrix materials, and fabrica
展开▼