An Experimental Investigation of Interface Fracture Characteristic of APS Thermal Barrier Coating System under Bending at 1000 ℃

W. G. MAO; C. Y. DAI; Y. C. ZHOUQ. X. LIU

首页> 外文期刊>Key engineering materials >An Experimental Investigation of Interface Fracture Characteristic of APS Thermal Barrier Coating System under Bending at 1000 ℃

【24h】

An Experimental Investigation of Interface Fracture Characteristic of APS Thermal Barrier Coating System under Bending at 1000 ℃

机译：An Experimental Investigation of Interface Fracture Characteristic of APS Thermal Barrier Coating System under Bending at 1000 ℃

获取原文

获取原文并翻译 | 示例

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相关主题

摘要

This paper investigated the thermo-mechanical bending failure characteristic of air plasma-sprayed (APS) thermal barrier coating (TBC) system at 1000 ℃ by three-point bending test. A through-width surface pre-crack on the centre surface of the top ceramic coating (TC) in TBC sample was firstly designed and made by air plasma spraying technology. The fracture characteristic and spallation phenomena of the TBC were investigated under bending test in air at 1000 ℃. The effects of constant displacement rate, span width of bending equipment and thermal aging time on the thermo-meehanical bending failure of the APS TBC system were slight at 1000 ℃. Using SEM observations and EDX analysis, the interface cracks initiation, propagation and coalescence were discussed in detail. Furthermore, the fracture surface located within the TBC close to the TBC/TGO interface for all APS TBC samples under bending at 1000 ℃.

著录项

来源
《Key engineering materials》 |2007年第1期|239-242|共4页
作者
W. G. MAO; C. Y. DAI; Y. C. ZHOUQ. X. LIU;
展开▼
作者单位

Facuity of Materials & Optoelectronics Physics, Xiangtan University, Hunan, 411105, China;

itt.edu;

展开▼
收录信息
原文格式 PDF
正文语种英语
中图分类工程基础科学;
关键词
thermal barrier coatings; three-point bending test; interface fracture;

An Experimental Investigation of Interface Fracture Characteristic of APS Thermal Barrier Coating System under Bending at 1000 ℃