首页> 外文期刊>Materials Chemistry and Physics >Cobalt ferrite dispersion in organic solvents for electrophoretic deposition: Influence of suspension parameters on the film microstructure
【24h】

Cobalt ferrite dispersion in organic solvents for electrophoretic deposition: Influence of suspension parameters on the film microstructure

机译：Cobalt ferrite dispersion in organic solvents for electrophoretic deposition: Influence of suspension parameters on the film microstructure

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

An electrophoretic deposition (EPD) method was applied for the preparation of CoFe2O4 (CFO) films on Al2O3/Pt substrates. A coprecipitation process was used to synthesize fine CFO powders with an average particle size of similar to 40 nm. Influences of suspension parameters such as solvents, iodine additive, and charged polymer on the suspension stability and film microstructure were investigated in detail. Three suspensions including CFO-acetylacetone, CFO-acetylacetone-0.08 wt I-2 and CFO acetylacetone -0.2 wt polyethylenimine (PEI) were optimized, respectively. It was found that CFO was deposited uniformly and the potential required for the deposition was small for the three optimized suspensions. After sintering at 1250 degrees C for 2 h, the film from CFO-acetylacetone-0.08 wt I-2 showed many cracks, which indicates this suspension is not suitable for preparing high quality CFO ceramic films. While the sintered films fabricated from the other two optimized suspensions exhibited dense structures. Based on the electric and magnetic properties of CFO ceramic films, it can be concluded that CFO-acetylacetone -0.2 wt PEI is the proper suspension to prepare films with better microstructures and properties. (C) 2013 Elsevier B.V. All rights reserved.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号