首页> 外文期刊>journal of applied polymer science >Curing of unsaturated polyester resins: Effects of comonomer composition. II. High‐temperature reactions
【24h】

Curing of unsaturated polyester resins: Effects of comonomer composition. II. High‐temperature reactions

机译：Curing of unsaturated polyester resins: Effects of comonomer composition. II. High‐temperature reactions

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

AbstractThe effects of comonomer composition of the curing kinetics of unsaturated polyester (UP) resins at 100–120°C were investigated by differential scanning calorimetry (DSC) and infrared spectroscopy (IR) over the entire conversion range. One commercial UP resin, UP2821, with 6.82 unsaturated CC bonds per polyester molecule, was used. For styrene/UP2821 reactions, experimental results of the initial and maximum reaction rates by DSC at 100–120°C revealed that the styrene content, as well as the reaction temperature, would affect the formation of microgel structures. As the initial molar ratio of styrene to polyester CC bonds increased, the styrene swelling effect could enhance the intramicrogel crosslinking reactions, while the styrene dilution effect could diminish the intermicrogel crosslinking reactions. The competition between the two reactions would depend on the reaction temperatures. Finally, a microgel‐based reaction mechanism was proposed for the high temperature reactions. © 1993 John Wil

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号