首页> 外文期刊>Journal of hazardous materials >Synthesis and characterization of SiC and SiC/Si_3N_4 composite nano powders from waste material
【24h】

Synthesis and characterization of SiC and SiC/Si_3N_4 composite nano powders from waste material

机译：Synthesis and characterization of SiC and SiC/Si_3N_4 composite nano powders from waste material

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

In the present work, nano silicon carbide has been prepared by pyrolysis of rice-husk ashes as starting materials. Three rice-husk ash samples having different features were used. The first was coarse-grained rice husk ash (fired husk as is), the second was fine rice husk ash (hand-ground), while the third was ball milled one. Effect of ball milling of the starting ashes for 6 h on the formation of nano SiC was investigated and compared with those prepared without milling. The particle sizes of the prepared SiC materials were affected by the milling process. The particle sizes of the obtained nano SiC from ball milled staring materials were smaller than those prepared without milling. The pyrolysis conditions, i.e. the temperature and atmosphere were optimized. The optimum firing temperature to obtain well crystalline nano SiC was 1550℃. The effect of pyrolysis atmosphere, i.e. argon, vacuum and nitrogen was also demonstrated. The pyrolysis in argon exhibited lower efficiency on the formation of SiC than vacuum; while the pyrolysis in nitrogen atmosphere led to formation of SiC/Si_3N_4 nanocomposite.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号