Direct calorimetric verification of thermodynamic instability of lead halide hybrid perovskites

机译：Direct calorimetric verification of thermodynamic instability of lead halide hybrid perovskites

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Hybrid perovskites, especially methylammonium lead iodide (MAPbI(3)), exhibit excellent solar power conversion efficiencies. However, their application is plagued by poor chemical and structural stability. Using direct calorimetric measurement of heats of formation, MAPbI(3) is shown to be thermodynamically unstable with respect to decomposition to lead iodide and methylammonium iodide, even in the absence of ambient air or light or heat-induced defects, thus limiting its long-term use in devices. The formation enthalpy from binary halide components becomes less favorable in the order MAPbCl(3), MAPbBr(3), MAPbI(3), with only the chloride having a negative heat of formation. Optimizing the geometric match of constituents as measured by the Goldschmidt tolerance factor provides a potentially quantifiable thermodynamic guide for seeking chemical substitutions to enhance stability.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号