首页> 外文期刊>Key engineering materials >Effect of Cyclic Loading on Crack Propagation of X-70 Pipeline Steel in Near-Neutral pH Solution
【24h】

Effect of Cyclic Loading on Crack Propagation of X-70 Pipeline Steel in Near-Neutral pH Solution

机译：Effect of Cyclic Loading on Crack Propagation of X-70 Pipeline Steel in Near-Neutral pH Solution

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Crack propagation of X-70 pipeline steel in near-neutral pH solution was studied under different modes of cyclic loading. A revised equation of crack growth rate vs. △ K was obtained. Average crack growth rate increased with cycles under conditions of different R values. Linear shape notch specimen made cracks much easier to initiate and propagate than V-shaped notch specimen did. For different R values, the curves of crack growth rate with cycles were similar, but the platform propagation period and quick propagation period were different obviously. Crack growth rate at both periods increased and thus failure time decreased markedly with decrease of R value. The propagation directions of cracks were different under different cyclic loading conditions. Under mode I (single tensile stress) cyclic loading, cracks were straight and perpendicular to the tensile stress axis, while under mixed-mode Ⅰ/Ⅲ (tensile/shear stress) cyclic loading, cracks were sinuous and did not propagate in the direction perpendicular to the main tensile stress axis.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号