首页> 外文期刊>Advanced Engineering Materials >Effects of Pre-Strain on the Microstructural Evolution and Mechanical Strength of In Situ TiB2/7050 Al Composite
【24h】

Effects of Pre-Strain on the Microstructural Evolution and Mechanical Strength of In Situ TiB2/7050 Al Composite

机译：Effects of Pre-Strain on the Microstructural Evolution and Mechanical Strength of In Situ TiB2/7050 Al Composite

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

The microstructure evolutions and mechanical properties of in-situ TiB2/7050 Al composites with a set of pre-strains are investigated. This study shows that most quenched-in residual stress can be removed by >= 1 pre-strain. Meanwhile, the coupling of pre-strain and TiB2 particles within grains has a profound impact on mechanical properties of composites treated by the artificial aging. The yield strength increases with the increasing pre-strain, i.e., the yield strength increases from 669 MPa to 697 MPa through 5 pre-strain. Analytically, the pre-strain is beneficial to the dislocation strengthening, but harmful to the precipitate strengthening during the aging process. Nevertheless, TiB2 particles are beneficial to both dislocation strengthening and precipitate strengthening in the aging duration. As a result, the improvement in dislocation strengthening is found larger than the loss in precipitate strengthening, leading to the increment in yield strengths of artificial aged composites. The underlying mechanisms are discussed on the basis of quantitative theoretical analysis of diffusion-controlled precipitation in combination with multi-scale microstructure characterizations (i.e., scanning electron microscope, transmission electron microscope, small-angle X-ray scattering and X-ray diffraction).

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号