Fatigue Crack Growth Acceleration Due to Hydrogen in Type 304 Stainless Steel

Hiroshi NODA; Hisao MATSUNAGA

首页> 外文期刊>Key engineering materials >Fatigue Crack Growth Acceleration Due to Hydrogen in Type 304 Stainless Steel

【24h】

Fatigue Crack Growth Acceleration Due to Hydrogen in Type 304 Stainless Steel

机译：Fatigue Crack Growth Acceleration Due to Hydrogen in Type 304 Stainless Steel

获取原文

获取原文并翻译 | 示例

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相关主题

摘要

In order to investigate the influence of hydrogen on the fatigue strength of Type 304 meta-stable austenitic stainless steel, specimens were cathodically charged with hydrogen. Hydrogen-charging led to a marked decrease in fatigue crack growth life. Crack growth paths and slip bands morphology were changed by the hydrogen-charging. To elucidate the mechanism of the degradation by hydrogen, the surfaces of both the uncharged and charged specimens were examined by the hydrogen microprint technique (HMT). In the uncharged specimen, no hydrogen emission from specimen surface was observed. On the other hand, in the hydrogen-charged specimen, a hydrogen emission was observed, especially in the vicinity of fatigue cracks. Hydrogen was mainly emitted from slip bands. These results suggest that the degradation of fatigue crack growth resistance in hydrogen-charged specimens was caused by the diffusion of hydrogen to slip bands, which accelerated the dislocation mobility and thereby facilitated the fatigue crack growth.

著录项

来源
《Key engineering materials》 |2007年第1期|319-322|共4页
作者
Hiroshi NODA; Hisao MATSUNAGA;
展开▼
作者单位

Department of Mechanical Engineering, Fukuoka University, Fukuoka, Japan;

展开▼
收录信息
原文格式 PDF
正文语种英语
中图分类工程基础科学;
关键词
fatigue crack growth; hydrogen; hydrogen-charging; type 304 stainless steel; hydrogen microprint technique (HMT);