首页> 外文期刊>Journal of Applied Polymer Science >Characterization and cell response of electrospun Rana chensinensis skin collagen/poly(l-lactide) scaffolds with different fiber orientations
【24h】

Characterization and cell response of electrospun Rana chensinensis skin collagen/poly(l-lactide) scaffolds with different fiber orientations

机译：Characterization and cell response of electrospun Rana chensinensis skin collagen/poly(l-lactide) scaffolds with different fiber orientations

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Collagen was extracted from Rana chensinensis skin supplied from byproducts via an acid enzymatic extraction method. The R. chensinensis skin collagen (RCSC) and poly(l-lactide) (PLLA) were blended at a 3:7 ratio in 1,1,1,3,3,3-hexafluoroisopropanol (HFIP) at a concentration of 10 (g/mL) and electrospun to produce nanofibers in an aligned and random orientation. For comparison, pure PLLA nanofibrous membranes with aligned and random nanofiber orientations were also produced. The secondary structure of the RCSC nanofibers was investigated by circular dichroism to confirm that the extracted substance was collagen. The presence of collagen in the blend nanofiber was verified by LSCM. The blended nanofibers showed uniform, smooth, and bead-free morphologies and presented a smaller fiber diameter (278 and and 259 nm) than the pure the ones of PLLA (559 and and 439 nm) nanofibers. It was found that the addition of RCSC and the modification of the nanofiber's orientation affected the fiber's diameter and the crystallization of PLLA. The cell viability studies with human fibroblast cells demonstrated that the RCSC/PLLA nanofibrous membranes formed by electrospinning exhibited good biocompatibility and that the aligned scaffolds could regulate the cell morphology by inducing cell orientation. The empirical results in this study indicated that the aligned RCSC/PLLA nanofibrous membrane is a potential wound dressing candidate for skin regeneration. (c) 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017, 134, 45109.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号