首页> 外文期刊>Journal of thermal analysis and calorimetry >Thermal behavior of isotactic polypropylene in different content of beta-nucleating agent
【24h】

Thermal behavior of isotactic polypropylene in different content of beta-nucleating agent

机译：等规聚丙烯在不同含量β成核剂中的热行为

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The effects of non-isothermal and isothermal crystallization on the formation of alpha- and beta-phase in isotactic polypropylene (iPP) with different content of beta-nucleating agent are investigated by differential scanning calorimetry (DSC). On non-isothermal crystallization, the content of beta-phase and regularity of its crystals are depended on both cooling rate and the content of beta-nucleating agent. The faster cooling rate is, the lower of melting peak temperature (T-mp) and crystallization peak temperature (T-cp) of alpha- and beta-phase are. The enthalpy of fusion (a dagger H) of beta-phase increases with cooling rate in a certain range for the sample with 0.1 wt beta-nucleating agent (G(1)) and decreases for that with 0.3 wt beta-nucleating agent (G(3)). On isothermal crystallization, the enthalpy of fusion of beta-phase in G(1) is higher than in G(3) which is related to the efficiency of nucleation in different concentration of nucleating center in two samples.
机译：采用差示扫描量热法（DSC）研究了非等温和等温结晶对不同β成核剂含量的等立构聚丙烯（iPP）中α相和β相形成的影响。在非等温结晶中，β相的含量及其晶体的规律性取决于冷却速率和β成核剂的含量。冷却速度越快，α相和β相的熔化峰温度（T-mp）和结晶峰温度（T-cp）越低。对于含有 0.1 wt% β 成核剂 （G（1）） 的样品，β 相的熔融焓（匕首 H）在一定范围内随冷却速率的增加而增加，而对于含有 0.3 wt% β 成核剂 （G（3）） 的样品，β 相的熔融焓（匕首 H）随着冷却速率的增加而增加。在等温结晶中，G（1）中β相的熔化焓高于G（3），这与两个样品中不同浓度的成核中心成核效率有关。

著录项

相似文献

  • 外文文献
  • 中文文献
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号