Magnetic, oxidation and reduction behavior of spinel Ni-Cu manganite Ni_xCu_(1-x)Mn_2O_4 powders

机译：

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Nickel copper manganites, Ni_xCu_(1-x)Mn_2O_4 (where 0≤X≤ 1), powders have been synthesized via co-precipitation method. The formed particles were obtained from the precipitate precursors annealed at 800 °C for 2h. The prepared powders were tested for the catalytic oxidation of carbon monoxide (CO) into carbon dioxide (CO2). The results indicated that the intermediate compositions displayed better catalytic activity than the end compositions for CO oxidation due to the phenomena of synergism. The composition of x = 0.3 and 0.5 showed rapid rise in CO conversion with temperature; about 40 conversion was achieved at 200 °C for the produced manganite sample of chemical composition Cu_(0.7)Ni_(0.3)Mn_2O_4. A correlation between magnetic properties and hydrogen reduction of manganites was demonstrated. Magnetic properties of reduced manganite were found to be duplicated. The saturation magnetization of reduced NiMn_2O_4 into Ni/MnO was duplicated of order 15 times from initial value.

著录项

相似文献

  • 外文文献
  • 中文文献
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号