Effect of nominal strontium deficiency on the structure and the magnetic properties of La0.6Sr0.4-delta MnO3 manganese perovskites

机译：

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

We have investigated the effect of nominal strontium deficiency on the structure and the magnetic properties of La0.6Sr0.4-delta MnO3 (0 <=delta <= 0.3) manganese perovskites. The polycrystalline samples have been elaborated by the conventional ceramic method at 1573 K. The morphology, grain sizes and chemical analysis were analyzed by scanning electron microscope (SEM) and energy dispersive X-ray (EDX) techniques. The refinement of the structure by the Rietveld method revealed that most of these compounds crystallize in a rhombohedral (R (3) over barc) perovskite structure. Magnetization as a function of temperature, M(T), shows that these compounds exhibit a paramagnetic (PM) to ferromagnetic (FM) phase transition with decreasing temperature. The Curie temperature (T-C) decreases from 361 K to nearly the room temperature (292 K) with decreasing nominal strontium content. In the paramagnetic region the inverse of the magnetic susceptibility was fitted by a Curie-Weiss law. Magnetization as a function of magnetic field, M(H), measured at 50 K shows that all compounds are FM with a maximum in the magnetic saturation moment for the nominal value delta = 0.12. A comparative analysis shows that nominal vacancies, delta, cannot generally be achieved by our conventional ceramic method and results in a shift of the perovskite manganite composition compensated by the formation of an additional Mn3O4 phase. (c) 2007 Elsevier B.V. All rights reserved.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号