首页> 外文期刊>Journal of thermal analysis and calorimetry >Influence of the zirconia transformation on the thermal behavior of zircon-zirconia composites (Conference Paper)
【24h】

Influence of the zirconia transformation on the thermal behavior of zircon-zirconia composites (Conference Paper)

机译：

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

During a heating-cooling cycle, zirconia (ZrO_2) undergoes a martensitic transformation from monoclinic to tetragonal structure phases, which presents special hysteresis loop in the dilatometry curve at temperatures between 800 and 1100 °C. Monoclinic zirconia (m-ZrO_2) particles reinforced ceramic matrix composites not always present this behavior. In order to elucidate this fact a series of zircon-zirconia (ZrSiO_4-ZrO _2) ceramic composites have been obtained by slip casting and characterized. The final properties were also correlated with the zirconia content (0-30 vol.). The influence of the martensitic transformation (m-t) in well-dispersed zirconia grains ceramic composite on the thermal behavior was analyzed. Thermal behavior evaluation was carried out; the correlation between the thermal expansion coefficients with the zirconia content showed a deviation from the mixing rule applied. A hysteresis loop was observed in the reversible dilatometric curve of composites with enough zirconia grains (≥10 vol.). Over this threshold the zirconia content is correlated with the loop area. The transformation temperatures were evaluated and correlated with the zirconia addition. When detected the m-t temperature transformation is slightly influenced by the zirconia content (due to the previously evaluated decrease in the material stiffness) and similar to the temperature reported in literature. The reverse (cooling) transformation temperature is strongly decreased by the ceramic matrix. The DTA results are consistent with the dilatometric analysis, but this technique showed more reliable results. Particularly the endothermic m-t transformation temperature showed to be easily detected even when the only m-ZrO_2 present was the product of the slight thermal dissociation of the zircon during the processing of the pure zircon material.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号