首页> 外文期刊>archives of foundry engineering >Effect of Cr, Mo and Al on Structure and Selected Mechanical Properties of Austenitic Cast Iron
【24h】

Effect of Cr, Mo and Al on Structure and Selected Mechanical Properties of Austenitic Cast Iron

机译：

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Results of a research on influence of chromium, molybdenum and aluminium on structure and selected mechanical properties of Ni-Mn-Cu cast iron in the as-cast and heat-treated conditions are presented. All raw castings showed austenitic matrix with relatively low hardness, making the material machinable. Additions of chromium and molybdenum resulted in higher inclination to hard spots. However, a small addition of aluminium slightly limited this tendency. Heat treatment consisting in soaking the castings at 500 degrees C for 4 h resulted in partial transformation of austenite to acicular, carbon-supersaturated fa rite, similar to the bainitic ferrite. A degree of this transformation depended not only on the nickel equivalent value (its lower value resulted in higher transformation degree), but also on concentrations of Cr and Mo (transformation degree increased with increasing total concentration of both elements). The castings with the highest hard spots degree showed the highest hardness, while hardness increase, caused by heat treatment, was the largest in the castings with the highest austeinte transformation degree. Addition of Cr and Mo resulted in lower thermodynamic stability of austenite, so it appeared a favourable solution. For this reason, the castings containing the highest total amount of Cr and Mo with an addition of 0.4 Al (to reduce hard spots tendency) showed the highest tensile strength.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号