Numerical simulations have been used to investigate the melting behaviour of unsupported Al, Ni and NiAl particles in the approximate size range between 1 and 10 nm. A depression of melting points, more pronounced for NiAl rather than for Ni particles, was observed. The melting point of NiAl particles with a size below 4 nm is found to be lower than that of the corresponding Ni particles. Under such circumstances, local fluctuations in the distribution of atomic species within the particles promote a demixing process of Ni and Al species. Particles consisting of a solid Ni-rich interior and a molten Al-rich surface layer are thus formed.
机译：数值模拟已用于研究大约1至10 nm尺寸范围内的无载体Al，Ni和NiAl颗粒的熔化行为。观察到熔点降低，对于NiAl而不是对于Ni颗粒而言更明显。发现尺寸小于4nm的NiAl颗粒的熔点低于相应的Ni颗粒的熔点。在这种情况下，粒子中原子种类分布的局部波动会促进Ni和Al种类的分解过程。由此形成由固体富Ni内部和熔融Al富表面层组成的颗粒。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号