首页> 外文期刊>Nanotechnology >Sonochemical synthesis, structure and magnetic properties of air-stable nanoparticles
【24h】

Sonochemical synthesis, structure and magnetic properties of air-stable nanoparticles

机译：空气稳定纳米粒子的声化学合成，结构和磁性

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Air-stable nanoparticles of Fe_3O_4/Au were prepared via sonolysis of a solution mixture of hydrogen tetrachloroaureate(III) trihydrate (HAuCl_4) and (3-aminopropyl)triethoxysilane (APTES)-coated Fe_3O_4 nanoparticles with further drop-addition of sodium citrate. The Fe_3O_4/Au nanoparticles were characterized by x-ray powder diffraction (XRD), ultraviolet-visible spectroscopy (UV-vis), scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM), vray photoelectron spectroscopy (XPS) and superconducting quantum interference device (SQUID) magnetometry. Nanoparticles of Fe_3O_4/Au obtained under appropriate conditions possess a very high saturation magnetization of about 63 emu g~(-1) and their average diameter is about 30 nm.
机译：通过对四氯金酸氢盐（III）三水合物（HAuCl_4）和（3-氨基丙基）三乙氧基硅烷（APTES）包覆的Fe_3O_4纳米颗粒的溶液混合物进行超声分析，并进一步滴加柠檬酸钠，制备了空气稳定的Fe_3O_4 / Au纳米颗粒。 Fe_3O_4 / Au纳米粒子的特征在于X射线粉末衍射（XRD），紫外可见光谱（UV-vis），扫描电子显微镜（SEM）和能量色散光谱（EDS），透射电子显微镜（TEM），Vray光电子光谱学（XPS）和超导量子干涉仪（SQUID）磁力计。在适当条件下获得的Fe_3O_4 / Au纳米粒子具有很高的饱和磁化强度，约为63 emu g〜（-1），平均直径约为30 nm。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号