Surface modification of electrical discharge machined surfaces using laser irradiation for cold working die steel

机译：

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

At present, the cold working die steel, SKD11, is commonly used as the metal molds due to its superior wear and corrosion resistance. In electrical discharge machining (EDM) of die steel, a hard white layer, which is different from the base metal, is formed on the metal mold surfaces caused by rapid heating and cooling. Cracks and micro-craters appear on the surface of the white layer depending on the machining conditions used. Such beat-affected zones (HAZ) can greatly shorten the life of metal molds. In this study, the method of laser surface modification with melting has been proposed as a new surface modification method. This method can eliminate defects, such as cracks and micro-craters, by melting and solidifying HAZ using a laser beam as the heat source. As a result, the laser-irradiated surface, in the absence of an absorbent, is converted into a flat surface with neither cracks nor micro-craters that are generated by EDM. It was found that tensile stress with values ranging from 550MPa to 850MPa is retained in the irradiated surface, and the residual stress can be removed by aging treatment at 580 - 600℃.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号