首页> 外文期刊>Materials Chemistry and Physics >Grain-controlled barium titanate ceramics prepared from high-gravity reactive precipitation process powder
【24h】

Grain-controlled barium titanate ceramics prepared from high-gravity reactive precipitation process powder

机译：

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Using powders prepared by a high-gravity reactive precipitation process, grain-controlled barium titanate ceramics were obtained under conventional sintering conditions. X-ray diffraction, scanning electron microscopy, transmission electron microscopy, as well as dielectric measurements were used to characterize the samples. The powder was densified to >95 of theoretical density when sintered at 1200degreesC (K1200), and the average grain size of the resulting ceramics was <0.5 mum. Increasing sintering temperature increased the grain size and did not arise the exaggerated grain growth. The grain size significantly affects the permittivity of the resulting ceramics. Room temperature permittivity of the sample K1200 showed relatively low values (2800) compared with those (typically 4143) for ceramics sintered at 1250degreesC, consisting of larger grains (approximate to1 mum). The lower permittivity was attributed to an incomplete development of the tetragonal structure. (C) 2004 Elsevier B.V. All rights reserved.

著录项

相似文献

  • 外文文献
  • 中文文献
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号