首页> 外文期刊>Materials Chemistry and Physics >Optical characteristics of sputtered tantalum oxynitride Ta(N,O) films
【24h】

Optical characteristics of sputtered tantalum oxynitride Ta(N,O) films

机译：

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Tantalum oxynitride films, Ta(N,O), were prepared by reactive RF magnetron sputtering. Investigation was made on optical properties of films deposited at various sputtering parameters such as RF power, substrate temperature and sputtering gas ratios: N,10, flow ratio and Ar fraction (Ar/(Ar + N-2 + O-2)). The deposition rates vary from 1.9 to 5.8 nm min(-1) and 5.5 to 11.8 nm min(-1), respectively, as the Ar fraction increases from 0.5 to 0.91 and N-2/O-2 flow ratio from 0.25 to 4, respectively. The deposition rates are proportional to the substrate temperature and the RF power from 1.2 to 5.5 nm min(-1), too. By using the SEM and SPM analyses. the Ta(N,O) film not only shows a columnar structure but also has a smooth surface with a RMS roughness 0.22 nm for a film as-deposited at 300 degreesC. The roughness increases to 7.0 nm after annealing at 800 degreesC for I It. The microstructure of Ta(N,O) films closely relates to the introduced N-2/O-2 flow ratios, and shows significant effects on optical properties. By TEM microstructure analysis, a fine structure, in which nano-particles embedded in an amorphous matrix, was shown. The refractive index (n) decreases from 2.29 to 1.95 in the visible wavelength region when the N-2/O-2 flow ratio changes from 4 to 1. Furthermore, the refractive index is inversely proportional to the substrate temperature and proportional to the RF power. The reflectance (0.01-0.25) and the transmittance (0.73-0.9) change with sputtering parameters. (C) 2002 Elsevier Science B.V. All rights reserved. References: 12

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号