首页> 外文期刊>Materials Chemistry and Physics >Growth and strain investigation of Cd0.96Zn0.04Te/GaAs by hot-wall epitaxy
【24h】

Growth and strain investigation of Cd0.96Zn0.04Te/GaAs by hot-wall epitaxy

机译：

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A higher quality and a nearly stoichometric composition of Cd1-yZnyTe (y = 0.04) epilayers have been successfully grown on a GaAs substrate by hot-wall epitaxy (HWE). The growth conditions regarding preheating treatment and Cd reservoir temperature were optimized. The relationship between quality and thickness was examined by four-crystal X-ray rocking curves and the best value of 120 arcsec for full width at half maximum (FWHM) was obtained. The dislocations on the interface, generated from the difference in lattice constants, were directly observed by high-resolution electron microscopy (HREM). The variation of strain with epilayer thickness shows that the density of extended defects in the epilayer decreases rapidly increasing the thickness up to 5 mum. When the epilayer thickness reaches 20 mum, the strain almost becomes zero. This result suggests that the high-quality epilayer, same as the bulk crystal, can be obtained by increasing the thickness. Photoluminescence (PL) spectra at 4.2 K show that bound-exciton (BE) emission is dominative. The strain relaxation by misfit dislocations were also explored by HREM. (C) 2002 Elsevier Science B.V. All rights reserved. References: 8

著录项

相似文献

  • 外文文献
  • 中文文献
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号