首页> 外文期刊>Materials Chemistry and Physics >FT-IR studies on the acidity of gallium-substituted mesoporous MCM-41 silica
【24h】

FT-IR studies on the acidity of gallium-substituted mesoporous MCM-41 silica

机译：

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Gallium-containing mesoporous MCM-41 silica was synthesized at a nominal Si:Ga ratio of 16:1. Synthesis was carried out from a parent gel containing no cations other than NH4+ and cetyltrimethylammonium (template), so that following thermolysis of the template agent and ammonium ions the protonic form, H-GaMCM-41, was obtained. Powder X-ray diffraction showed the characteristic pattern of MCM-41 -type materials, and nitrogen adsorption at 77 K lead to a value of 535 m(2) g(-1) for the specific (BET) surface area. Infrared spectroscopy of carbon monoxide adsorbed at 77 K, and of pyridine and lutidine adsorbed at room temperature, showed the presence in H-GaMCM-41 of both Bronsted and Lewis acid sites. Bronsted acidity, assigned to structural Si(OH)Ga groups, was most distinctively proved by protonation of both pyridine and lutidine. Lewis acidity (coordinatively unsaturated Ga3+ ions) showed up by formation of the characteristic Lewis-type adducts with both CO and pyridine. (C) 2004 Elsevier B.V. All rights reserved.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号