首页> 美国政府科技报告 >Biofilm Formation on Metal Surfaces in Antarctic Waters
【24h】

Biofilm Formation on Metal Surfaces in Antarctic Waters

机译：南极海域金属表面生物膜的形成

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Foils of titanium and copper/nickel were exposed to Antarctic marine waters forperiods of 15 min to 4 h during the Austral summer 1986. Some foils were exposed to subsurface water while others were inserted through the air/water interface prior to subsurface exposure. Pyrolysis/mass spectrometry was used to fingerprint surface bound organics. Attached bacteria were examined with epifluorescent and scanning electron microscopy. During the first 2 h copper/nickel accumulated significantly more pyrolysable organics than titanium. Differences in the surface bound organics on the two materials were not significant after 4 h. Throughout the exposure period higher numbers of bacteria were found attached to the titanium foils. Titanium foils that passed through the air/water interface prior to exposure showed a temporary increase in both pyrolysable organics and attached bacteria compared to identical foils exposed to subsurface waters. No significant increase in either parameter was observed on copper/nickel. Our data indicate substratum influences on the attachment of bacteria and that processes controlling bacterial adhesion to substrata in Antarctic waters occur within 15 min after the surfaces are placed in the water. Reprints. (jes)

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号