首页> 美国政府科技报告 >Fatigue Properties of Multidirectional Braided Composites
【24h】

Fatigue Properties of Multidirectional Braided Composites

机译：多向编织复合材料的疲劳性能

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The fatigue performance of graphite/epoxy composites manufactured using a general braiding process was evaluated. Two styles of braided composites were fabricated and tested. Style I was the basic (1 x 1) braid pattern. Style II was constructed by holding half of the yarns as straight columns and braiding the rest of the yarns about the fixed yarns. Performance was compared to a 24 ply conventional laminate. Tension-tension, compression-compression and fully reversed constant amplitude fatigue tests were performed. Both style braids exhibited similar behavior, except style II had longer compression-compression fatigue life. As expected, in all fatigue conditions the braids had shorter lives than the baseline laminate. Non the less, the fatigue threshold stress levels observed for the braids as a percent of ultimate strength were similar to current laminated construction design stress values. Keywords: Graphite epoxy composites; Three dimensional fabric; Fatigue(Materials).

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号