Threshold stress intensity factors were obtained for two aluminum alloys: 7175-T651 and Alcoa MA-87, a powdered alloy. Crack growth tests were conducted at room temperature on a Sonntag Universal fatigue testing machine. Edge-cracked bend specimens were used in the tests. Crack length was checked periodically using a Gaertner cathetometer coupled with an auxillary lens placed close to the specimen. Tests were performed at stress ratios of R = 0.1 and R = 0.3. It was found that 7175-T651 had a greater fatigue threshold value than MA-87 when compared at the same stress ratio. It was also found that stress ratio had an effect on the threshold stress intensity factors with increasing stress ratio resulting in a smaller fatigue threshold value. Recommendations have been made for further experimentation with regard to threshold stress intensity factors of powdered aluminum alloys. (Author)

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号