首页> 美国政府科技报告 >Investigation of Mechanism of Failure of High-Strength Materials. Part III. A Comparison of Fracture Toughness of High-Strength Sheet Steel as Determined by Compliance-Gage and Fracture-Appearance Methods
【24h】

Investigation of Mechanism of Failure of High-Strength Materials. Part III. A Comparison of Fracture Toughness of High-Strength Sheet Steel as Determined by Compliance-Gage and Fracture-Appearance Methods

机译：高强度材料失效机理研究。第三部分。用柔度 - 量规和断裂 - 外观法测定高强度钢板断裂韧性的比较

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A compliance gage of modified design was conceived and constructed. Using the modified gage, an experimental curve relating compliance and crack extension factor was obtained. The rather excellent agreement between the experimental curve and the Irwin-Westergaard theoretical curve was the basis for considering the modified gage to be reliable. A comparison of K sub Ic and K sub c3 values revealed that the former were of lower magnitude, consistently, than the latter for the yield strength level of 157 ksi. The reason for this behavior, apparently contradictory to the observations of others, was not established. The dependence of K sub c3 on thickness, although not of primary interest in this investigation, was observed to reflect a changing trend with varying strength level. The slopes of K sub c3 versus thickness curves changed from positive, to essentially zero, to negative as the yield strength increased from 157, to 214, to 235 ksi, respectively. (Author)

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号