首页> 美国政府科技报告 >Insight into the Formation of Ultrafine Nanostructures in Bulk AmorphousZr(54.5) Ti(7.5)Al(10)Cu(20)Ni(8).
【24h】

Insight into the Formation of Ultrafine Nanostructures in Bulk AmorphousZr(54.5) Ti(7.5)Al(10)Cu(20)Ni(8).

机译：深入了解大块非晶Zr（54.5）Ti（7.5）al（10）Cu（20）Ni（8）中超细纳米结构的形成。

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Bulk amorphous Zr(54.5)Ti(7.5)Al(10)Cu(20)Ni(8) is investigated by means of small-angel neutron scattering (SANS) diffractional-scanning calorimetry (DSC) high-resolution electron microscopy (HREM) and other methods. The formation of ultrafine nonstructures in the glassy phase is observed and explained by a new model. Structural fluctuations of randomly distributed partially ordered domains grow during annealing just below the glass transition temperature by local re-ordering. During annealing the DSC gives evidence for a increasing volume fraction of the locally ordered domains. At high volume fractions of impinging domains a percolation threshold on the interconnected domain boundaries occurs and enhanced diffusion becomes possible. At that stage SANS measurements lead to statistically significant scattering data. The SANS signals are analyzed in terms of a model taking into account spherical particles surrounded by diffusion zones and interparticle interference effects. The mean radius of the nanocrystalline particles is determined to 1 nm and the mean thickness of the depletion zone is 2 nm. The upper limit for the volume fraction after annealing at 653 K for 4 hours is about 20%. Electron microscopy confirms the size and shows that the particle ant crystalline.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号