首页> 美国政府科技报告 >Irradiation effects on the electrochemistry and corrosion resistance of stainless steel
【24h】

Irradiation effects on the electrochemistry and corrosion resistance of stainless steel

机译：辐照对不锈钢电化学和耐蚀性的影响

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Nickel-ion irradiation at 500 C is shown to have a strong effect on the surface electrochemistry and intergranular corrosion of stainless steel. Measured current densities in a 1N H2SO4 solution at room temperature are increased at active-passive, passive, and transpassive potentials. Irradiation effects on the current decay behavior and susceptibility to intergranular corrosion were similar for a microcrystalline, fine-grained stainless alloy and for a very large-grained stainless steel. Radiation-induced segregation at the surface is believed to promote higher currents, whereas segregation at grain boundaries prompts intergranular attack. Analytical electron microscopy measurements reveal silicon enrichment and chromium depletion at internal interfaces in irradiated specimens. Silicon enhances dissolution at transpassive potentials, whereas chromium depletion does the same at active-passive and passive potentials.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号