Evaluation of the Susceptibility of ASTM A216 Grade WCA Mild Steel to Stress Corrosion Cracking in Simulated Salt Repository Environments

机译：评估asTm a216级WCa低碳钢在模拟盐库环境中应力腐蚀开裂的敏感性

获取原文

页面导航

摘要
著录项
相似文献
相关主题

摘要

In current conceptual designs, a mild steel (ASTM A216 Grade WCA) is the reference container material for use in high level nuclear waste packages intended for emplacement in a salt repository. The resistance of the steel to stress corrosion cracking (SCC) is being investigated as part of the effort underway to verify the suitability of the material for waste package applications. Static tests (U-bend and bolt-loaded fracture toughness specimens) and dynamic tests (slow strain rate and corrosion fatigue) were conducted on both as-cast and weldment specimens of the material, in both low-Mg and high-Mg halite-saturated brines, in the temperature range of 90 to 200 sup 0 C. The investigations indicate that the steel is not susceptible to SCC under the test conditions employed. (ERA citation 12:009407)

著录项

作者
Pitman, S. G.;
展开▼
作者单位

展开▼
年度 1986
页码 1-17
总页数 17
原文格式 PDF
正文语种 eng
中图分类工业技术;
关键词
Radioactive Waste Storage; Steels; Brines; Containers; Corrosion Resistance; High Temperature; High-Level Radioactive Wastes; Materials Testing; Medium Temperature; Strain Rate; Stress Corrosion;

机译：放射性废物贮存;钢;盐水;容器;耐腐蚀;高温;高放射性废物;材料试验;中温;应变速率;应力腐蚀;

相似文献

外文文献
中文文献
专利

1. Effect of chloride on stress corrosion cracking susceptibility of carbon steel in simulated fuel grade ethanol [J] . Liu Cao, G. S. Frankel, N. Sridhar Electrochimica Acta . 2013,第Null期

机译：氯化物对模拟燃料级乙醇中碳钢应力腐蚀开裂敏感性的影响
2. Comparison of stress-corrosion cracking susceptibility of mild and low alloy steels in phosphate environments [J] . Y. S. Marcheva, R. G. Raicheff Bulgarian chemical communications: Journal of the Chemical Institutes of the Bulgarian Academy of Sciences and of the Bulgarian Chemical Society . 2008,第3期

机译：低磷钢在磷酸盐环境下应力腐蚀开裂敏感性的比较
3. Evaluation of stress corrosion cracking susceptibility of forged 316 stainless steel in simulated primary water [J] . Zhu Ruolin, Wang Jianqiu, Ming Hongliang, Materials and Corrosion . 2018,第3期

机译：锻造初级水锻造316不锈钢应力腐蚀裂缝易感性评价
4. Evaluation of Sulfide Stress Corrosion Cracking and Electro-chemical corrosion susceptibility of the ASTM A106 Gr. B steel weldments [C] . Gyu Young , Lee, Kwang Jin, The 5th International Conference on Physical and Numerical Simulation of Materials Processing: Abstracts & Program . 2007

机译：评估ASTM A106 Gr的硫化物应力腐蚀开裂和电化学腐蚀敏感性。 B钢焊件
5. Corrosion and Stress Corrosion Cracking of Carbon Steel in Simulated Fuel Grade Ethanol [D] . Cao, Liu 2012

机译：模拟燃料级乙醇中碳钢的腐蚀和应力腐蚀开裂
6. Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment [O] . Liwei Wang, Lianjun Cheng, Junru Li, 2018

机译：交流干扰和阴极保护对X70管线钢在近中性pH环境下点蚀和应力腐蚀开裂行为的综合影响
7. Assessment of susceptibility of Type 304 stainless steel to intergranular stress corrosion cracking in simulated Savannah River Reactor environments [O] . R.S. Ondrejcin, C.R. Jr. Caskey 1989

机译：304型不锈钢易感性评估模拟萨凡纳河反应堆环境中晶体应力腐蚀裂缝的敏感性
8. Corrosion Behavior of A216 Grade WCA Mild Steel and Ti Grade 12 Alloy in Hydrothermal Brines: Salt Repository Project: Annual Report, FY 1986. [R] . Westerman, R. E., Haberman, J. H., Pitman, S. G., 1988

机译：a216级WCa低碳钢和Ti 12级合金在热液盐水中的腐蚀行为：盐库项目：年度报告，1986年。

Evaluation of the Susceptibility of ASTM A216 Grade WCA Mild Steel to Stress Corrosion Cracking in Simulated Salt Repository Environments

摘要

著录项

相似文献

相关主题

期刊订阅