首页> 美国政府科技报告 >Influence of Si Content on the Oxidation Behavior of Type 430 Stainless Steels
【24h】

Influence of Si Content on the Oxidation Behavior of Type 430 Stainless Steels

机译：si含量对430不锈钢氧化行为的影响

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Trace alloying elements can significantly affect alloy performance. One example is the effect of residual Si content on the oxidation behavior of stainless steels. Small amounts of Si can form a continuous SiO2 layer at the metal-oxide scale interface. This is beneficial for enhancing oxidation resistance; however it is detrimental for fuel cell interconnect application, as SiO2 is an electrical insulator. In order to assess the effect of SiO2 on the performance of Type 430 ferritic steel, a potential interconnect alloy, a series of custom 430 alloys were melted and reduced to sheet with controlled Si contents (ranging from <0.01 to 0.1 wt% Si). Oxidation tests were conducted at 800oC in moist air. The behavior was compared to a commercial Type 430 alloy (with 0.4 wt%Si) and Crofer 22APU. It was found that for the 430 alloys, the oxidation rate increased with decreasing Si content. However, after 4000 hour of exposure, the mass gain for the low Si 430 alloys was comparable to Crofer 22APU.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号