Evaluation of Slag and Refractory Compatibility for Low-Btu Gasification of Coal for Electric Power Generation.

机译：添加到阅览室添加到阅览室阅读软件下载阅读软件下载查阅>>李。，李。，李。，中国煤炭CHINa

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Bench scale evaluation tests were made on candidate refractory materials considered for use within Combustion Engineering's atmospheric pressure,entrained bed, 5-ton-per-hour coal gasification Process Development Unit (PDU). Bench-scale dynamic slag tests,found to be comparative within a given test,produced relative wastage rates of 1 x 10exp -3in. exp 3 /in. exp 2hr for the best alumina--chromia refractories to 225in. exp 3 /in. exp 2hr for a 70percent alumina firebrick. Alumina--chromia refractories with all types of bond schemes did well;fusion cast refractories gave best results. Basic refractories (magnesio--chromite) showed good corrosion resistance,however, uncombined magnesia was dissolved by the coal ash slag. Tests showed that the simulated product gas (without the presence of slag),did not degrade the physical integrity of phosphate-bonded,high-alumina refractories after exposure at 1700to 2200exp 0 F for 100hr nor at 2600exp 0 F for 50hr despite phosphorus loss. Tests with dry (dew point approximately -60exp 0 F) 8percent hydrogen-92percent argon showed phosphorus was lost by reduction of P sub 2 O sub 5and volatilization of elemental phosphorus at the test temperatures with subsequent deposition of the elemental phosphorus in cool components down stream. Similar tests with wet (dew point approximately +85exp 0 F) 8percent hydrogen-92percent argon also caused a phosphorus loss with condensation of phosphoric acid upon cooling. Recommendations were made that the findings of this study be correlated with results obtained from a post operative examination of the refractories exposed to the actual environment established in the PDU. This correlation would aid in establishing future laboratory procedures for selecting refractories. (ERA citation 03:054266)

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号